Crack injection set 4 PUR Steel

Crack inejctions set 4 Steel PUR

For repaire of cracks in basement walls, concrete floors, concrete walls and many more.

Rising Restoration Kit 4 PUR consists of:

• 3x1 liter can PU resin
  • 2-component polyurethane resin - Elastic injection resin and coating resin - solvent-free
  • For non-positive bonding of cracks and different building materials with each other. In the mixture is a milky-turbid liquid of relatively low viscosity.
• Product description: SEE BELOW
• 1x injection press 500ml
  • with hose 300mm and gripping coupling for nipples at the injection packer
• 25x steel drill packer with HD high pressure niplle h DIN 71412
  • ø10mm x ca 75mm long
• 1x safety glasses UV clear with soft-touch strap
• 1x pair of high quality Showa 160PVC gloves
• 1x drive-in-bolt H1A for grease nipples

3 liters of polyurethane resin are sufficient for approx. 8 to 10 meters of cracking.
Precise details are not possible regarding the nature, the depth, the masonry, etc.

Application areas:

• is used for elastic sealing of cracks, imperfections, voids, expansion and working joints in civil engineering.
• is used in all types of structures and building structures.
• is suitable for filling in the casting or low pressure process, as well as for crack injection in the medium to high pressure process.
• seals properly against pressurized water.
• is also used as an elastic, wear-resistant coating material.

Mode of action / properties:

• Cures after processing to a Schrumoffreien, permanently elastic polymer
• retains its elasticity even at minus degrees
• Like all polyurethanes, it has a fantastic flank adhesion and can be applied to dry, damp or wet flanks
• is absolutely weather-resistant and offers excellent resistance to chemicals
• Like all PU materials, it tends to yellow and is not UV stable
• is completely physiologically and ecologically harmless in the hardened state.

Officially tested by the Technical University of Munich - drinking water approval

Technical Data:

• Material Base: solvent-free 2-component polyurethane resin
• Appearance: milky, cloudy, liquid
• Viscosity Mixture: approx. 500 mPas

Density (20°C):

• Component A: 1.00kg/l
• Component B: 1.22kg/l
• Mixture: 1.03kg/l
• Comp.A / Comp.B: 6:1
• Comp.A / Comp.B: 7,3:1

Mixing ratios bundle 7kgs:
                         Comp.A     Comp.B
2kgs                 1,71kgs   :    0,29kgs
3kgs                 2,57kgs   :    0,43kgs
4kgs                 3,43kgs   :    0,57kgs
5kgs                 4,29kgs   :    0,71kgs
6kgs                 5,14kgs   :    0,86kgs

Features:

• Processing Time (20°C): about 45 minutes
• Processing Temperature (Material Temperature): not less than 8°C
• Hardening: approx. 4 hours
• Accessibility: approx. 12 hours
• Curing: about 7 days
• Shore A hardness: approx. 70
• Elongation at break: 60%
• Young's modulus: 4.0 N / mm²
• Consumption: 100-500 g / running meter depending on the crack width
• Storage: dry conditions, away from direct sunlight
• Storability: 1 year in airtight containers
• Delivery form: 1kg and 7kg tinplate containers