Crack inejctions set 3 Steel POX

For repaire of cracks in basement walls, concrete floors, concrete walls and many more.

Rising Restoration Kit 3 POX consists of:

• 3x1 liter can POX I Injection resin and mortar resin
  - 2-component epoxy resin for frictionally bonding cracks and different building materials among each other
  - for the production of high-strength chemical-resistant epoxy heart and mortar
  

• 1x injection press 500ml
       - with hose 300mm and gripping coupling for nipples at the injection packer

• 25x steel drill packer with HD high pressure niplle h DIN 71412
   - ø10mm x ca 75mm long
  

• 1x Safety glasses UV clear with soft-touch strap

• 1x Pair of high quality Showa 160PVC gloves
  
  
• 1x drive-in-bolt H1A for grease nipples
  
  

3 liters of epoxy resin are sufficient for approx. 8 to 10 meters of cracking. Precise details are not possible regarding the nature, the depth, the masonry, etc.

Description for epoxy resin

Pox I - Injection and Resin Mortar - 2-component epoxy resin - for frictionally bonding of cracks and various materials to each other - for the manufacture of high-strength chemical resistant epoxy resin and mortar
Product description: Pox I is a solvent-free, unfilled, transparent 2-component epoxy resin with high compressive and tensile strength
Application Field: Pox I is used for the frictional and adhesive sealing and injection of concrete, masonry, wood and natural stone. Pox I adheres extremely well to dry, damp and wet surfaces, cures even under water without affecting the resin properties. Furthermore you can use Pox I also for manufacturing Bonding agents, coatings, highly wear-resistant thin and thick coatings, waterproofing and industrial flooring

Function / Features: The mixed components to cure a hard elastic thermosets with high compressive, flexural, adhesive tensile and shear strength. Due to the special, mature formulation Pox I liables on dry and wet conditions very good. Pox I is highly chemical resistant, non-toxic when cured and non-toxic

Officially tested by the Technical University of Munich - drinking water approval

Technical Data:
Material Base: solvent-free 2-component epoxy resin
Appearance: honey-yellow, transparent
Viscosity (20°C): about 270mPas

Density (20°C)
Component A: 1.12kg/l
Component B: 1.03kg/l
Mixture: 1.07kg/l
Comp.A / Comp.B: 2:1
Comp.A / Comp.B: 2,2:1

Mixing ratios bundle 6kgs:
                         Comp.A     Comp.B
1kgs                 0,67kgs   :    0,33kgs
2kgs                 1,34kgs   :    0,67kgs
3kgs                 2,00kgs   :    1,00kgs
4kgs                 2,67kgs   :    1,33kgs
5kgs                 3,33kgs   :    1,66kgs

Mixing ratios bundle 12kgs:
                         Comp.A     Comp.B
6kgs                 4,00kgs   :    2,00kgs
7kgs                 4,67kgs   :    2,33kgs
8kgs                 5,33kgs   :    2,67kgs
9kgs                 6,00kgs   :    3,00kgs
10kgs               6,77kgs   :    3,33kgs
11kgs               7,33kgs   :    3,67kgs

Processing Time (20°C): about 40 minutes in an approach of 1 kg
Processing Temperature (Material Temperature): not less than 5°C
Curing Time (20°C): about 12 hours, final strength after 7 days
Compressive Strength: 89,6N/mm²
Flexural Strength: 31,9N/mm²
Shear Strength by concrete bonding
6,33 N/mm² (Bonding and dry storage)
4,06 N/mm² (Bonding and dry storage)
Storage: dry conditions, away from direct sunlight
Storability: 1 year in unopened containers
Hazardous Goods (November 2012): Component A - UN3082, Component B - UN1760

All technical data relate to laboratory conditions 20°C / 65%. r. F.